New insights into the electrochemical performance of precursor derived Si(Nb)OC composites as anode materials for batteries.

This work represents a first attempt to synthesize Si(Nb)OC ceramic composites through the polymer pyrolysis or the precursor-derived ceramics (PDC) route for use as a hybrid anode material for lithium-ion batteries (LIB). Electron microscopy, X-ray diffraction, and various spectroscopy techniques were used to examine the micro/nano structural features and phase evolution during cross-linking, pyrolysis, and annealing stages. During the polymer-to-ceramic transformation process, in situ formation of carbon (so-called "free carbon"), and crystallization of t -NbO 2 , NbC phases in the amorphous Si(Nb)OC ceramic matrix are identified. The first-cycle reversible capacities of 431 mA h g -1 and 256 mA h g -1 for the as-pyrolyzed and annealed Si(Nb)OC electrodes, respectively, exceeded the theoretical Li capacity of niobium pentaoxide or m -Nb 2 O 5 (at approximately 220 mA h g -1 ). With an average reversible capacity of 200 mA h g -1 and close to 100% cycling efficiency, as-pyrolyzed Si(Nb)OC demonstrates good rate capability. X-ray amorphous SiOC with uniformly distributed nanosized Nb 2 O 5 and graphitic carbon structure likely provides stability during repeated Li + cycling and the formation of a stable secondary electrolyte interphase (SEI) layer, leading to high efficiency.