Synthesis of Zeolitic Mo-Doped Vanadotungstates and Their Catalytic Activity for Low-Temperature NH3-SCR.

Mo was successfully introduced into a vanadotungstate (VT-1), which is a crystalline microporous zeolitic transition-metal oxide based on cubane clusters [W4O16]8- and VO2+ linkers (MoxW4-x. x: number of Mo in VT-1 unit cell determined by inductively coupled plasma-atomic emission spectroscopy (ICP-AES)). It was confirmed that W in the cubane units was substituted by Mo. The resulting materials showed higher microporosity compared with VT-1. The surface area and the micropore volume increased to 296 m2·g-1 and 0.097 cm3·g-1, respectively, for Mo0.6W3.4 compared with the those values for VT-1 (249 m2·g-1 and 0.078 cm3·g-1, respectively). The introduction of Mo changed the acid properties including the acid amount (VT-1: 1.06 mmol g-1, Mo0.6W3.4: 2.18 mmol·g-1) and its strength because of the changes of the chemical bonding in the framework structure. MoxW4-x showed substantial catalytic activity for the selective catalytic reduction of NO with NH3 (NH3-selective catalytic reduction (SCR)) at a temperature as low as 150 °C.