Fluorine-Free, Highly Durable Waterproof and Breathable Fibrous Membrane with Self-Clean Performance.

Lightweight, durable waterproof and breathable membranes with multifunctional properties that mimic nature have great potential for application in high-performance textiles, efficient filtering systems and flexible electronic devices. In this work, the fluoride-free triblock copolymer poly(styrene-b-butadiene-b-styrene) (SBS) fibrous membrane with excellent elastic performance was prepared using electrospinning. According to the bionics of lotus leaves, a coarse structure was built onto the surface of the SBS fiber using dip-coating of silicon dioxide nanoparticles (SiO 2 NPs). Polydopamine, an efficient interfacial adhesive, was introduced between the SBS fiber and SiO 2 NPs. The hydrophobicity of the modified nanofibrous membrane was highly improved, which exhibited a super-hydrophobic surface with a water contact angle large than 160°. The modified membrane retained super-hydrophobic properties after 50 stretching cycles under 100% strains. Compared with the SBS nanofibrous membrane, the hydrostatic pressure and WVT rate of the SBS/PDA/SiO 2 nanofibrous membrane improved simultaneously, which were 84.2 kPa and 6.4 kg·m -2 ·d -1 with increases of 34.7% and 56.1%, respectively. In addition, the SBS/PDA/SiO 2 nanofibrous membrane showed outstanding self-cleaning and windproof characteristics. The high-performance fibrous membrane provides a new solution for personal protective equipment.