Diffusion Barrier Properties of the Intermetallic Compound Layers Formed in the Pt Nanoparticles Alloyed Sn-58Bi Solder Joints Reacted with ENIG and ENEPIG Surface Finishes.

Pt-nanoparticle (NP)-alloyed Sn-58Bi solders were reacted with electroless nickel-immersion gold (ENIG) and electroless nickel-electroless palladium-immersion gold (ENEPIG) surface finishes. We investigated formation of intermetallic compounds (IMCs) and their diffusion barrier properties at reaction interfaces as functions of Pt NP content in the composite solders and duration of solid-state aging at 100 °C. At Sn-58Bi-xPt/ENIG interfaces, typical Ni 3 Sn 4 /Ni 3 P(P-rich layer) microstructure was formed. With the large consumption of the Ni-P layer, the Ni-P and Cu layers were intermixed and Cu atoms spread over the composite solder after 500 h of aging. By contrast, a (Pd,Ni)Sn 4 /thin Ni 3 Sn 4 microstructure was observed at the Sn-58Bi-xPt/ENEPIG interfaces. The (Pd,Ni)Sn 4 IMC effectively suppressed the consumption of the Ni-P layer and Ni 3 Sn 4 growth, functioning as a good diffusion barrier. Therefore, the Sn-58Bi-xPt/ENEPIG joint survived 500 h of aging without microstructural degradation. Based on the experimental results and analysis of this study, Sn-58Bi-0.05Pt/ENEPIG is suggested as the optimum combination for future low-temperature soldering systems.