Intermetallic PtFe Electrocatalysts for the Oxygen Reduction Reaction: Ordering Degree-Dependent Performance.

Tian-Wei SongMing-Xi ChenPeng YinLei TongMing ZuoSheng-Qi ChuPing ChenHai-Wei Liang
Published in: Small (Weinheim an der Bergstrasse, Germany) (2022)
Platinum-based atomically ordered alloys (i.e., intermetallic compounds) have distinct advantages over disordered solid solution counterparts in boosting the cathodic oxygen-reduction reaction (ORR) in proton-exchange-membrane fuel cells. Nevertheless, the pivotal role of ordering degree of intermetallic catalysts in promoting ORR performance has been ignored heavily so far, probably owing to the lack of synthetic routes for controlling the ordering degree, especially for preparing highly ordered intermetallic catalysts. Herein, a family of intermetallic PtFe catalysts with similar particle size of 3-4 nm but varied ordering degree in a wide range of 10-70% are prepared. After constructing the PtFe/Pt core/shell structure with around 3 Pt-layer skin, a positive correlation between the ordering degree of the intermetallic catalysts and their ORR activity and durability is identified. Notably, the highly ordered PtFe/Pt catalyst exhibits a high mass activity of 0.92 A mg Pt -1 at 0.9 V iR-corrected as cathode catalyst in H 2 -O 2 fuel cell, with only 24% loss after accelerated durability tests. The ordering degree-dependent performance can be ascribed to the compressive strain effect induced by the intermetallic PtFe core with smaller lattice parameters, and the more thermodynamically stable intermetallic structure compared to disordered alloys.
Keyphrases
  • highly efficient
  • metal organic framework
  • room temperature
  • induced apoptosis
  • transition metal
  • ionic liquid
  • stem cells
  • signaling pathway
  • carbon dioxide
  • bone marrow
  • cell cycle arrest
  • electron transfer