Fullerene-Liquid-Crystal Induced Micrometer-Scale Charge-Carrier Diffusion in Organic Bulk Heterojunction.

The short charge carrier diffusion length (L D ) (100-300 nm) in organic bulk heterojunction (BHJ) impedes the further improvement in power conversion efficiency (PCE) of organic solar cells (OSCs), especially for thick-film (> 400 nm) devices matching with industrial solution processing. Here we develop a facile method to efficiently increase L D and then improve PCEs of OSCs via introducing a fullerene liquid crystal, F1, into active layer. F1 combines the inherent high electron mobility of fullerene and strong self-assembly capacity of liquid crystal, providing fast channel for charge-carrier transport, and reducing energetic disorder and trap density in BHJ film via enhancing crystallization. Typically, in PM6:Y6:F1 BHJ, the enhanced charge carrier mobility (> 10 -2 cm -2 V -1 s -1 ) and prolonged charge carrier lifetime (55.3 μs) are acquired to realize the record L D of 1.6 μm or 2.4 μm for electron or hole, respectively, which are much higher than those of PM6:Y6 binary sample, and comparable to and even better than those values reported for some inorganic/hybrid materials, such as CuIn x Ga (1-x) Se 2 (CIGS) and perovskite thin films. Profiting from the micrometer-scale L D , the PM6:Y6:F1 ternary OSCs sustain a remarkable PCE of 15.23% with the active layer thickness approaching 500 nm. This article is protected by copyright. All rights reserved.