Development of a novel Eu 2+ activated oxonitridosilicate cyan phosphor for enhancing the color quality of a violet-chip-based white LED.

Cyan phosphors are urgently needed to fill the cyan gap and improve the spectral continuity of white light-emitting diodes (LEDs) to cater to the high demand for high-quality lighting. Here, a series of new Eu 2+ -activated La 3 Si 6.5 Al 1.5 N 9.5 O 5.5 (LSANO) cyan phosphors were prepared, and their luminescence properties and color centers were analyzed through fluorescence spectral measurements from 7 K to 475 K. At 300 K, the photoluminescence excitation (PLE) spectrum monitored at 483 nm presents a broadband of 200-460 nm with a peak at 398 nm, matching well with commercial violet LED chips. When excited by 398 nm violet light, the photoluminescence emission (PL) spectrum of LSANO:0.01Eu 2+ exhibits a cyan emission band at about 483 nm. At 7 K, the emission spectrum clearly shows an asymmetric emission band and the emission peak wavelength changes from 483 nm (300 K) to 500 nm (7 K), indicating that there are two possible color centers in the LSANO:Eu 2+ phosphor. Moreover, the maximum emission value can be adjusted from 480 to 499 nm by adjusting the doping content of Eu 2+ . Finally, a violet-chip-based white LED with the optimized color quality of R a = 91.4, R f = 90.1, and R g = 93.6 was fabricated by adding the prepared cyan phosphor, verifying the potential application of the prepared cyan phosphor LSANO:Eu 2+ in high-quality white LEDs.