High Oxygen Sensitivity of TiO 2 Thin Films Deposited by ALD.
Aleksei V AlmaevNikita N YakovlevDmitry A AlmaevMaksim G VerkholetovGrigory A RudakovKristina I LitvinovaPublished in: Micromachines (2023)
The gas sensitivity and structural properties of TiO 2 thin films deposited by plasma-enhanced atomic layer deposition (ALD) were examined in detail. The TiO 2 thin films are deposited using Tetrakis(dimethylamido)titanium(IV) and oxygen plasma at 300 °C on SiO 2 substrates followed by annealing at temperatures of 800 °C. Gas sensitivity under exposure to O 2 within the temperature range from 30 °C to 700 °C was studied. The ALD-deposited TiO 2 thin films demonstrated high responses to O 2 in the dynamic range from 0.1 to 100 vol. % and low concentrations of H 2 , NO 2 . The ALD deposition allowed the enhancement of sensitivity of TiO 2 thin films to gases. The greatest response of TiO 2 thin films to O 2 was observed at a temperature of 500 °C and was 41.5 arb. un. under exposure to 10 vol. % of O 2 . The responses of TiO 2 thin films to 0.1 vol. % of H 2 and 7 × 10 -4 vol. % of NO 2 at a temperature of 500 °C were 10.49 arb. un. and 10.79 arb. un., correspondingly. The resistance of the films increased due to the chemisorption of oxygen molecules on their surface that decreased the thickness of the conduction channel between the metal contacts. It was suggested that there are two types of adsorption centers on the TiO 2 thin films surface: oxygen is chemisorbed in the form of O 2- on the first one and O - on the second one.