Effect of ultrasonic agitation on marginal adaptation, intratubular penetration and bonding strength of calcium-silicate-based endodontic sealers: A laboratory study.

The effect of ultrasonic activation (UA) on marginal adaptation, intratubular penetration and bond strength provided by three calcium silicate-based sealers was evaluated. Ninety-six distobuccal root canals of maxillary molars were randomly divided into 8 groups (n = 12) according to the sealer and UA application: EndoSequence BC sealer (ESBC), Sealer Plus BC (SPBC) and Bio-C Sealer (BCS), using AH Plus (AH) as a control group. The specimens were sectioned at 2, 4 and 6 mm from the apex. The data were statistically analysed using Kruskall-Wallis, Dunn, Mann-Whitney and chi-squared tests. UA improved the marginal adaptation of ESBC (6 mm), SPBC (all levels), BCS (2/4 mm) and AH (4 mm) (p < 0.05); the bond strength of SBPC (2 mm) and BCS (6 mm) were also improved (p < 0.05). The UA of endodontic silicate-based sealers improved the marginal adaptation in all levels and the bond strength of SBPC and BCS sealer.