Dual-Silane Premodified Silica Nanoparticles-Synthesis and Interplay between Chemical, Mechanical, and Curing Properties of Silica-Rubber Nanocomposites: Application to Tire Tread Compounds.

In silica-rubber based nanocomposites, a single organo-silicon is often used to compatibilize and covalently link silica to rubber. In this work, we have investigated the impact, at micro- and macroscales, of the decoupling of the hydrophobization and the coupling activity of silane by pretreating silica with two different silane chemistries. The first one, a mercaptosilane, is the coupling agent that promotes a covalent link between silica and rubber during the sulfur-mediated vulcanization reaction. The second one, an alkylsilane, aims to improve the silica dispersion. For both kind of silanes, we have varied the chain length and studied at macroscale the dynamic mechanical properties through the key indicators that are E '' as loss modulus, E ' as storage modulus, and their respective ratio tan δ. The shorter silanes combination yielded an improvement in terms of wet grip indicators with tan δ at 0 °C increasing from 0.205 to 0.237 while maintaining rolling resistance indicators at the same level. We have evaluated the impact of the silane chemistry onto the cross-linking reactivity within the fabricated rubber-based nanocomposites by using moving-dye rheometer measurements (MDR). By purposely using atomic force microscopy (AFM), we have studied the silica dispersion in the matrix and the rubber/silica interface and provided the rationale explanation of the mechanical properties observed at the macroscale. AFM observation pointed out the existence of a soft interface around silica fillers when long alkylsilanes were used. We infer that this interface impacts the polymer-filler dynamic and subsequently affects the mechanical properties of the composite material.