Ultralow Friction Self-Lubricating Nanocomposites with Mesoporous Metal-Organic Frameworks as Smart Nanocontainers for Lubricants.

Smart nanocontainers with stimuli-responsive property can be used to fabricate a new kind of self-lubricating nanocomposite, while the practical potential of the metal-organic frameworks (MOFs) as nanocontainers for lubricants has not been realized. In this work, mesoporous Cu-BTC MOFs storing oleylamine nanocomposites were explored from synthesis and microstructure to self-lubricating characterization. The stress stimuli-responsiveness behavior of the Cu-BTC storing oleylamine (Cu-BTCO) for lubrication has been investigated by subjecting it to macroscopic ball-on-disc friction tests. The steady-state coefficients of friction (COFs) of the Cu-BTC nanocomposites without lubricants were ca. 0.5. In contrast, after oleylamine as the lubricant was incorporated into the Cu-BTC container in the nanocomposite, ultralow friction (COF, ca. 0.03) was achieved. It has been demonstrated that the improved lubricating performance was associated with the lubricating film which was in situ produced by the chemical reaction between the oleylamine released from the nanocontainer and the friction pairs. Therefore, the nanocomposite with smart Cu-BTC container holds the promise of realizing extraordinary self-lubricating properties under stress stimuli.