Improved Thermal Stability and Enhanced Thermoelectric Properties of p-Type BaCu 2 Te 2 by Doping of Cl.

Doping in semiconductors is a widely implemented strategy for manipulation of carrier concentration, which is a critical parameter to regulate the thermoelectric performance. Stoichiometric BaCu 2 Te 2 shows high hole concentration and unstable transport properties owing to the inherent Cu vacancy and dynamic precipitation behavior. In this work, Te has been partially substituted by Cl in BaCu 2 Te 2 to suppress the overhigh hole concentration. Due to the high electronegativity of Cl, strong Cl-Cu bonds can significantly inhibit the Cu migration and the consequent dynamic precipitation. Meanwhile, nano-precipitate BaCl 2 distributes in the grain boundary, acting as ionic blocking layers. Therefore, the thermal stability of the samples can be essentially improved via chemical bonding strengthening and grain boundary engineering. In terms of thermal transport, the introduced point defects and second phase strengthen the short-wavelength and medium-wavelength phonon scattering, leading to further reduced thermal conductivity. Eventually, the repeatable ZT value of BaCu 2 Te 1.98 Cl 0.02 reached 1.22 at 823 K, which is higher by 19.6% compared with 1.02 of pristine BaCu 2 Te 2 . The average ZT s of BaCu 2 Te 2- x Cl x ( x = 0, 0.02, 0.04, and 0.06) in the temperature range of 323-823 K are 0.737 for x = 0.02, 0.689 for x = 0.04, and 0.667 for x = 0.06, which are 24.6, 17.2, and 13.4% higher than the average ZT of 0.588 corresponding to the undoped sample, respectively. The study shows that synergetic enhancements of thermal stability and thermoelectric properties can be achieved by strengthening chemical bonding and constructing ionic blocking layers in the grain boundary, which can be applied to other fast-ionic conductor thermoelectric materials.