Manufacturing of Aluminum Nano-Composites Reinforced with Nano-Copper and High Graphene Ratios Using Hot Pressing Technique.

In this study, the nano-aluminum powder was reinforced with a hybrid of copper and graphene nanoplatelets (GNPs). The ratios of GNPs were 0 wt%, 0.4 wt%, 0.6 wt%, 1.2 wt% and 1.8 wt%. To avoid the reaction between aluminum and graphene and, consequently, the formation of aluminum carbide, the GNP was first metalized with 5 wt% Ag and then coated with the predetermined 15 wt% Cu by the electroless coating process. In addition, the coating process was performed to improve the poor wettability between metal and ceramic. The Al/(GNPs-Ag)Cu nanocomposites with a high relative density of 99.9% were successfully prepared by the powder hot-pressing techniques. The effects of (GNPs/Ag) and Cu on the microstructure, density, hardness, and compressive strength of the Al-Cu nanocomposite were studied. As a result of agitating the GNPs during the cleaning and silver and Cu-plating, a homogeneous distribution was achieved. Some layers formed nano-tubes. The Al 4 C 3 phase was not detected due to coating GNPs with Cu. The Cu 9 Al 4 intermetallic was formed during the sintering process. The homogeneous dispersion of Cu and different ratios of GNs, good adhesion, and the formation of the new Cu 9 Al 4 intermetallic improved in hardness. The pure aluminum sample recorded 216.2 HV, whereas Al/Cu reinforced with 1.8 GNs recorded 328.42 HV with a 51.9% increment. The compressive stress of graphene samples was improved upon increasing the GNPs contents. The Al-Cu/1.8 GNs sample recorded 266.99 MPa.