Investigation of the Performance of Hastelloy X as Potential Bipolar Plate Materials in Proton Exchange Membrane Fuel Cells.

The phase, mechanical properties, corrosion resistance, hydrophobicity, and interfacial contact resistance of Hastelloy X were investigated to evaluate its performance in proton exchange membrane fuel cells (PEMFCs). For comparison, the corresponding performance of 304 stainless steel (304SS) was also tested. Hastelloy X exhibited a single-phase face-centered cubic structure with a yield strength of 445.5 MPa and a hardness of 262.7 HV. Both Hastelloy X and 304SS exhibited poor hydrophobicity because the water contact angles were all below 80°. In a simulated PEMFC working environment (0.5 M H 2 SO 4 + 2 ppm HF, 80 °C, H 2 ), Hastelloy X exhibited better corrosion resistance than 304SS. At 140 N·cm -2 , the interfacial contact resistance of Hastelloy X can reach as low as 7.4 mΩ·cm 2 . Considering its overall performance, Hastelloy X has better potential application than 304SS as bipolar plate material in PEMFCs.