In Situ Observation of Lithiation and Delithiation Reactions of a Silicon Thin Film Electrode for All-Solid-State Lithium-Ion Batteries by X-ray Photoelectron Spectroscopy.

In situ X-ray photoelectron spectroscopy is applied to electrochemical lithiation/delithiation processes of an amorphous Si electrode sputter-deposited on a Li6.6La3Zr1.6Ta0.4O12 solid electrolyte. After the first lithiation, a broad Li peak appears at the Si surface, and peaks corresponding to bulk Si and Si suboxide significantly shift to lower binding energy. The appearance of the Li peak and shift of the Si peaks confirm the formation of lithium-silicide and lithium-silicates due to the lithiation of Si and native suboxide. The composition of lithium-silicide is estimated to be Li3.44Si by quantitative analysis of electrochemical response and photoelectron spectra. Peak fitting analysis shows the formation of Li2O and Li2CO3 due to side reactions. Upon the following delithiation, the peak corresponding to Li3.44Si phase shifts back to higher binding energy to form Li0.15Si phase, while lithium-silicates, Li2O, and Li2CO3 remained as irreversible species. Thus, electrochemical reactions accompanied with lithiation/delithiation processes are successfully observed.