Strong and Stable Magnetorheological Fluids Based on Flaky Sendust-Co0.4Fe0.4Ni0.2 Nanocomposite Particles.

The magnetorheological (MR) performance of suspensions based on magnetic (flaky Sendust (FS))-magnetic (Co0.4Fe0.4Ni0.2) nanocomposite particles was investigated by using a vibrating sample magnetometer and a rotational rheometer. Flaky Sendust@Co0.4Fe0.4Ni0.2 nanocomposite particles were fabricated through wet chemical synthesis of Co0.4Fe0.4Ni0.2 on the surface of FS. The density of the resultant FS@Co0.4Fe0.4Ni0.2 was less than that of FS due to the pore/void formation in the composite particles. Because of the high saturation magnetization of Co0.4Fe0.4Ni0.2 (165 emu/g), FS@Co0.4Fe0.4Ni0.2 (145 emu/g) exhibited greater magnetization than bare FS (130 emu/g), which resulted in the good performance of FS@Co0.4Fe0.4Ni0.2-based MR fluids: the suspension exhibited a remarkably high yield stress, almost one order greater than that of MR fluids based on hierarchically structured (HS) Fe3O4 particles. In addition, the high drag coefficient of FS@Co0.4Fe0.4Ni0.2 in the liquid medium, in conjunction with its lower density, resulted in a substantially improved long-term stability, better than that of Co0.4Fe0.4Ni0.2- or FS-based suspensions. Although the density of the FS@Co0.4Fe0.4Ni0.2 nanoparticles is higher than that of HS-Fe3O4 particles, their stability is much better than the stability of HS-Fe3O4 particle's suspension. Manufactured magnetic-magnetic nanocomposite particles provide a feasible MR suspension of high MR performance and long-term stability.