Anion-Containing Solvation Structure Reconfiguration Enables Wide-Temperature Electrolyte for High-Energy-Density Lithium-Metal Batteries.

The demand for high-energy-density lithium batteries (LBs) that work under a wide temperature range (-40 to 60 °C) has been increasing recently. However, the conventional lithium hexafluorophosphate (LiPF 6 )-based ester electrolyte with a solvent-based solvation structure has limited the practical application of LBs under extreme temperature conditions. In this work, a novel localized high-concentration electrolyte (LHCE) system is designed to achieve the anion-containing solvation structure with less free solvent molecules using lithium difluorophosphate (LiPO 2 F 2 ) as a lithium salt, which enables wide-temperature electrolyte for LBs. The optimized solvation structure contributes to the cathode-electrolyte interface (CEI) with abundant LiF and P-O components on the surface of the LiNi 0.5 Co 0.2 Mn 0.3 O 2 (NCM523) cathode, effectively inhibiting the decomposition of electrolyte and the dissolution of transition-metal ions (TMIs). Moreover, the weakened Li + -dipole interaction is also beneficial to the desolvation process. Therefore, the 4.3 V Li||NCM523 cell using the modified electrolyte maintains a high capacity retention of 81.0% after 200 cycles under 60 °C. Meanwhile, a considerable capacity of 70.9 mAh g -1 (42.0% of that at room temperature) can be released at an extremely low temperature of -60 °C. This modified electrolyte dramatically enhances the electrochemical stability of NCM523 cells by regulating the solvation structure, providing guidelines for designing a multifunctional electrolyte that works under a wide temperature range.