High-Entropy Alloy Electrocatalysts Bidirectionally Promote Lithium Polysulfide Conversions for Long-Cycle-Life Lithium-Sulfur Batteries.

High-entropy alloys (HEAs) have attracted considerable attention, owing to their exceptional characteristics and high configurational entropy. Recent findings demonstrated that incorporating HEAs into sulfur cathodes can alleviate the shuttling effect of lithium polysulfides (LiPSs) and accelerate their redox reactions. Herein, we synthesized nano Pt 0.25 Cu 0.25 Fe 0.15 Co 0.15 Ni 0.2 HEAs on hollow carbons (HCs; denoted as HEA/HC) by a facile pyrolysis strategy. The HEA/HC nanostructures were further integrated into hypha carbon nanobelts (HCNBs). The solid-solution phase formed by the uniform mixture of the five metal elements, i.e., Pt 0.25 Cu 0.25 Fe 0.15 Co 0.15 Ni 0.2 HEAs, gave rise to a strong interaction between neighboring atoms in different metals, resulting in their adsorption energy transformation across a wide, multipeak, and nearly continuous spectrum. Meanwhile, the HEAs exhibited numerous active sites on their surface, which is beneficial to catalyzing the cascade conversion of LiPSs. Combining density functional theory (DFT) calculations with detailed experimental investigations, the prepared HEAs bidirectionally catalyze the cascade reactions of LiPSs and boost their conversion reaction rates. S/HEA@HC/HCNB cathodes achieved a low 0.034% decay rate for 2000 cycles at 1.0 C. Notably, the S/HEA@HC/HCNB cathode delivered a high initial areal capacity of 10.2 mAh cm -2 with a sulfur loading of 9 mg cm -2 at 0.1 C. The assembled pouch cell exhibited a capacity of 1077.9 mAh g -1 at the first discharge at 0.1 C. The capacity declined to 71.3% after 43 cycles at 0.1 C. In this work, we propose to utilize HEAs as catalysts not only to improve the cycling stability of lithium-sulfur batteries, but also to promote HEAs in energy storage applications.