P2/O3 Biphasic Cathode Material through Magnesium Substitution for Sodium-Ion Batteries.

P2-type Fe-Mn-based oxides offer excellent discharge specific capacity and are as affordable as typical layered oxide cathode materials for sodium-ion batteries (SIBs). After Cu modification, though they can improve the cycling performance and air stability, the discharge specific capacity will be reduced. Considering the complementary nature of biphasic phases in electrochemistry, hybridizing P2/O3 hybrid phases can enhance both the storage performance of the battery and specific capacity. Herein, a hybrid phase composite with high capacity and good cycle performance is deliberately designed and successfully prepared by controlling the amount of Mg doping in the layered oxide. It has been found that the introduction of Mg can activate anion redox in the oxide layer, resulting in a significant increase in the specific discharge capacity of the material. Meanwhile, the dual-phase structure can produce an interlocking effect, thus effectively alleviating structure strain. The degradation of cycling performance caused by structural damage during the high-voltage charging and discharging process is clearly mitigated. The results show that the specific discharge capacity of Na 0.67 Cu 0.2 Mg 0.1 Fe 0.2 Mn 0.5 O 2 is as high as 212.0 mAh g -1 at 0.1C rate and 186.2 mAh g -1 at 0.2C rate. After 80 cycles, the capacity can still maintain 88.1%. Moreover, the capacity and cycle performance as well as the stability can still remain stable even in the high-voltage window. Therefore, this work offers an insightful exploration for the development of composite cathode materials for SIBs.