Novel Fluorinated Anion Exchange Membranes Based on Poly(Pentafluorophenyl-Carbazole) with High Ionic Conductivity and Alkaline Stability for Fuel Cell Applications.

Constructing good microphase separation structures by designing different polymer backbones and ion-conducting groups is an effective strategy to improve the ionic conductivity and chemical stability of anion exchange membranes (AEMs). In this study, a series of AEMs based on the poly(pentafluorophenylcarbazole) backbone grafted with different cationic groups were designed and prepared to construct well-defined microphase separation morphology and improved the trade-off between the properties of AEMs. Highly hydrophobic fluorinated backbone and alkyl spaces enhance phase separation and construct interconnected hydrophilic channels for anion transport. The ionic conductivity of the PC-PF-QA membrane was 123 mS cm -1 at 80 °C, and the ionic conductivity of the PC-PF-QA membrane decreased by only 6% after 960 h of immersion at 60 °C in 1 M NaOH aqueous solution. The maximum peak power density of the single cell based on PC-PF-QA was 214 mW cm -2 at 60 °C. This article is protected by copyright. All rights reserved.