Tailoring Pseudo-Graphitic Domain by Molybdenum Modification to Boost Sodium Storage Capacity and Durability for Hard Carbon.

Hard carbon (HC) stands out as the most prospective anode for sodium-ion batteries (SIBs) with significant potential for commercial applications. However, some long-standing and intractable obstacles, like low first coulombic efficiency (ICE), poor rate capability, storage capacity, and cycling stability, have severely hindered the conversion process from laboratory to commercialization. The above-mentioned issues are closely related to Na + transfer kinetics, surface chemistry, and internal pseudo-graphitic carbon content. Herein, constructing molybdenum-modified hard carbon solid spheres (Mo 2 C/HC-5.0), both the ion transfer kinetics, surface chemistry, and internal pseudo-graphitic carbon content are comprehensively improved. Specifically, Mo 2 C/HC-5.0 with higher pseudo-graphitic carbon content provides a large number of active sites and a more stable layer structure, resulting in improved sodium storage capacity, rate performance, and cycling stability. Moreover, the lower defect density and specific surface area of Mo 2 C/HC-5.0 further enhance ICE and sodium storage capacity. Consequently, the Mo 2 C/HC-5.0 anode achieves a high capacity of 410.7 mA h g -1 and an ICE of 83.9% at 50 mA g -1 . Furthermore, the material exhibits exceptional rate capability and cycling stability, maintaining a capacity of 202.8 mA h g -1 at 2 A g -1 and 214.9 mA h g -1 after 800 cycles at 1 A g -1 .