Influence of Copper on the Microstructural, Mechanical, and Biological Properties of Commercially Pure Zn-Based Alloys for a Potential Biodegradable Implant.

Three Zn-based alloys (Zn1Cu, Zn2Cu, and Zn3Cu) were developed by the addition of Cu (1, 2, and 3 wt %) into commercially pure Zn. This report systematically investigates the potential for these newly developed Zn-based alloys as biodegradable materials. Microstructural studies reveal the presence of spherical-shaped nanosized precipitates of ε-CuZn 4 in the Zn1Cu alloy, whereas Zn2Cu and Zn3Cu alloys exhibit the presence of both micron- and nanosized precipitates of ε-CuZn 4 . The mechanical properties such as hardness, tensile and compressive strengths improve significantly with an increase in the amount of Cu in the alloy. The Zn3Cu alloy exhibits the highest yield strength (225 ± 9 MPa) and ultimate tensile strength (330 ± 12 MPa) among all of the alloys, which are ∼2.7 and 2 times higher than those of pure Zn. In vitro degradation behavior is evaluated by the potentiodynamic polarization study and immersion testing in Hank's solution for 20 and 75 days. The corrosion rate after both polarization and immersion testing follows the order of pure Zn < Zn1Cu < Zn3Cu < Zn2Cu. An electrochemical impedance spectroscopy (EIS) study also concludes that Zn2Cu shows the lowest corrosion resistance. The % cell viability values of 3T3 fibroblasts cells after 5 days of culture in a 50% diluted extract of pure Zn, Zn2Cu, and Zn3Cu alloys are 76 ± 0.024, 86.18 ± 0.033, and 92.9 ± 0.026%, respectively, establishing the improved cytocompatibility of the alloys as compared to pure Zn. Furthermore, an antibacterial study also reveals that the Zn3Cu alloy exhibits 80, 67, and 100% increases in the zone of inhibition (ZOI) for Escherichia coli , Bacillus subtilis , and Pseudomonas aeruginosa bacteria, respectively, as compared to that of pure Zn.