Cyclic Penta-Twinned Rhodium Nanobranches as Superior Catalysts for Ethanol Electro-oxidation.
Jiawei ZhangJinyu YeQiyuan FanYating JiangYifan ZhuHuiqi LiZhenming CaoQin KuangJun ChengJun ZhengZhao-Xiong XiePublished in: Journal of the American Chemical Society (2018)
Developing active and durable electro-catalysts toward ethanol oxidation reaction (EOR) with high selectivity toward the C-C bond cleavage is an important issue for the commercialization of direct ethanol fuel cell. Unfortunately, current ethanol oxidation electro-catalysts (e.g., Pt, Pd) still suffer from poor selectivity for direct oxidation of ethanol to CO2, and rapid activity degradation. Here we report a facile route to the synthesis of a new kind of cyclic penta-twinned (CPT) Rh nanostructures that are self-supported nanobranches (NBs) built with 1-dimension CPT nanorods as subunits. Structurally, the as-prepared Rh NBs possess high percentage of open {100} facets with significant CPT-induced lattice strains. With these unique structural characteristics, the as-prepared CPT Rh NBs exhibit outstanding electrocatalytic performance toward EOR in alkaline solution. Most strikingly, the selectivity of complete conversion ethanol to CO2 on the CPT Rh NBs is measured to be as high as 14.5 ± 1.1% at -0.15 V, far exceeding that for single-crystal tetrahedral nanocrystals, icosahedral nanocrystals, and commercial Rh black, as well as majority of reported values for Pt or Pd-based electro-catalysts. By combining with density functional theory calculation, the effects of different structural features of Rh on EOR are definitively elucidated. It was found that the large amount of open Rh (100) facets dominantly contribute to the outstanding activity and exceptionally high selectivity, while the additional tensile strain on (100) planes can further boost the catalytic activity by enhancing the adsorption strength and lowering the reaction barrier of dehydrogenation process of ethanol. As a proof of concept, the present work shows that rationally optimizing surface and electronic structure of electro-catalysts by simultaneously engineering their surface and bulk structures is a promising strategy to promote the performance of electro-catalysts.
Keyphrases
- highly efficient
- transition metal
- metal organic framework
- high speed
- density functional theory
- hydrogen peroxide
- electron transfer
- minimally invasive
- reduced graphene oxide
- stem cells
- high resolution
- molecular dynamics
- nitric oxide
- high glucose
- oxidative stress
- quantum dots
- transcription factor
- mesenchymal stem cells
- structural basis
- endothelial cells
- dna binding