Ultrahigh photo-stable all-inorganic perovskite nanocrystals and their robust random lasing.
Liuli YangTing WangQiuhong MinChaojie PiFan LiXiao YangKongzhai LiDacheng ZhouJian-Bei QiuXue YuXu-Hui XuPublished in: Nanoscale advances (2020)
Photo-instability has prevented further commercialization of all-inorganic perovskite nanocrystals (NCs) in the field of high-power optoelectronics. Here, an accelerated transformation process from non-luminescent Cs 4 PbBr 6 to CsPbBr 3 NCs with bright green emission is explored with irradiation at 365 nm during water-triggered structural transformation. The photoelectric field provided by the photon energy of 365 nm promotes the rapid stripping of CsBr and atomic reconstruction, contributing to the production of ultrahigh photo-stable defect-free CsPbBr 3 NCs. The robust emission output of the as-obtained CsPbBr 3 NCs is well preserved even when recorded after 160 min. Moreover, a long-term stable random lasing could be achieved when excited using an ∼800 nm femtosecond laser for at least 8.6 × 10 7 laser shots. Our results not only elucidate the photo-induced accelerated phase transformation process of the all-inorganic perovskites, but also open up opportunities to synthesize highly stable CsPbBr 3 NCs for their practical application in photovoltaics and optoelectronics.