Accurate X-ray diffraction data required for proper evaluation of bond valence sums and global instability indexes: redetermination of the crystal structures of diamond-like Cu 2 CdSiS 4 and Cu 2 HgSnS 4 as a case study.
Megan M TreeceJordan C KellyKate E RoselloAndrew J CraigJennifer A AitkenPublished in: Acta crystallographica. Section C, Structural chemistry (2023)
Our calculations of the global instability index (G) values for some diamond-like materials with the general formula I 2 -II-IV-VI 4 have indicated that the structures may be unstable or incorrectly determined. To compute the G value of a given compound, the bond valence sums (BVSs) must first be calculated using a crystal structure. Two examples of compounds with high G values, based on data from the literature, are the wurtz-stannite-type dicopper cadmium silicon tetrasulfide (Cu 2 CdSiS 4 ) and the stannite-type dicopper mercury tin tetrasulfide (Cu 2 HgSnS 4 ), which were first reported in 1967 and 1965, respectively. In the present study, Cu 2 CdSiS 4 and Cu 2 HgSnS 4 were prepared by solid-state synthesis at 1000 and 900 °C, respectively. The phase purity was assessed by powder X-ray diffraction. Optical diffuse reflectance UV/Vis/NIR spectroscopy was used to estimate the optical bandgaps of 2.52 and 0.83 eV for Cu 2 CdSiS 4 and Cu 2 HgSnS 4 , respectively. The structures were solved and refined using single-crystal X-ray diffraction data. The structure type of Cu 2 CdSiS 4 was confirmed, where Cd 2+ , Si 4+ and two of the three crystallographically unique S 2- ions lie on a mirror plane. The structure type of Cu 2 HgSnS 4 was also verified, where all ions lie on special positions. The S 2- ion resides on a mirror plane, the Cu + ion is situated on a fourfold rotary inversion axis and both the Hg 2+ and the Sn 4+ ions are located on the intersection of a fourfold rotary inversion axis, a mirror plane and a twofold rotation axis. Using the crystal structures solved and refined here, the G values were reassessed and found to be in the range that indicates reasonable strain for a stable crystal structure. This work, together with some examples gathered from the literature, shows that accurate data collected on modern instrumentation should be used to reliably calculate BVSs and G values.
Keyphrases
- aqueous solution
- crystal structure
- high resolution
- metal organic framework
- electronic health record
- systematic review
- solid state
- big data
- magnetic resonance imaging
- computed tomography
- low grade
- magnetic resonance
- drug delivery
- high grade
- preterm infants
- quantum dots
- artificial intelligence
- contrast enhanced
- fluorescent probe