Robust Waterborne Superhydrophobic Coatings with Reinforced Composite Interfaces.

Waterborne superhydrophobic coatings have attracted tremendous attention recently, but their practical applications are severely limited by hydrophobic instability and poor mechanical durability. Herein, a novel robust waterborne PTFE-CP&MgO-AOP superhydrophobic coating was successfully fabricated by reinforcing composite interfaces. Combined with the self-polymerization of dopamine and the in situ grown MgO, CNTs-polydopamine&MgO (CP&MgO) particles with improved interfacial compatibility were obtained. Through the cross-linking and hydrogen bonding interactions, phosphate networks (CP&MgO-AOP) with the aluminum orthophosphate (AOP) binder were formed during dehydration polymerization. The phosphate networks not only enhanced the interfacial interaction among CP&MgO to form coral-like structures but also strengthened the interfacial binding force between the waterborne polytetrafluoroethylene (PTFE) coating and the substrate. With the enhanced composite interfacial strength, the waterborne PTFE-CP&MgO-AOP coating exhibited excellent wear-resistance, which can withstand more than 1.27 × 105 abrasion cycles. Moreover, the chemical bonding between the functional groups of phosphate networks and metal substrate improved the adhesion strength from grade 5 to 1. Furthermore, the prepared coating surface with the reticular/coral-like composite structures can lock the stable gas layer to maintain excellent hydrophobic stability, even under the conditions of strong acidic/alkaline, high-temperature, xenon lamp irradiation, and mechanical wear. Thus, this study is expected to open new insights into interfacial enhancement of robust waterborne superhydrophobic coatings.