Sulfonium-Functionalized Polystyrene-Based Nonchemically Amplified Resists Enabling Sub-13 nm Nanolithography.

Nonchemically amplified resists based on triphenyl sulfonium triflate-modified polystyrene (PSTS) were prepared by a facile method of modification of polystyrene with sulfonium groups. The uploading of the sulfonium group can be well-controlled by changing the feed ratio of raw materials, resulting in PSTS 0.5 and PSTS 0.7 resists with sulfonium ratios of 50 and 70%, respectively. The optimum developer (methyl isobutyl ketone/ethanol = 1:7) is obtained by analyzing contrast curves of electron beam lithography (EBL). PSTS 0.7 exhibits a better resolution (18 nm half-pitch (HP)) than the PSTS 0.5 resist (20 nm HP) at the same developing conditions for EBL. This novel resist platform was further evaluated by extreme ultraviolet lithography, and patterning performance down to 13 nm HP at a dose of 186 mJ cm -2 with a line edge roughness of 2.8 nm was achieved. Our detailed study of the reaction and patterning mechanism suggests that the decomposition of the polar triflate and triphenyl sulfonium groups into nonpolar sulfide or polystyrene plays an important role in the solubility switch.