Impact of Cellulolytic Fungi on Biodegradation of Hemp Shives and Corn Starch-Based Composites with Different Flame-Retardants.

Biocomposite boards (BcBs) composed of hemp shives and corn starch are known as thermal insulating or structural building materials. Therefore, they must be stable during exploitation. However, BcBs are exposed to microorganisms present in the environment, and it is of great interest to investigate the biodegradation behaviour of these materials. This work identified microorganisms growing on BcBs that contain either Flovan CGN or expandable graphite as flame retardants and selected fungi such as Rhizopus oryzae and Aspergillus fumigatus to test the way they affect the materials of interest. For this purpose, the enzymatic activity of cellulases and amylases produced by these organisms were determined. In addition, the apparent density as well as compressive strength of the affected boards were evaluated. The results showed that apparent density and compressive strength deteriorated in BcB composition with the Flovan CGN flame retardant. At the same time, the level of deterioration was lower when the expandable graphite was used, suggesting that it also acts as an antimicrobial agent. A scanning electronic microscopy analysis was employed to monitor the growth of microorganisms in the BcBs. Such analysis demonstrated that, regardless of BcB composition, fungi easily penetrate into the middle layers of the material.