Influence of Novel Experimental Light-Cured Resin Cement on Microtensile Bond Strength.

The purpose of this study was to evaluate the microtensile bond strength (µTBS) and Knoop hardness number (KHN) of a novel experimental light-cured resin cement (HL). Eighteen flat dentin surfaces of human molars were polished using #600 SiC paper and bonded to CAD/CAM resin blocks with the respective resin cements and composites: HL, Panavia V5 (PV), and Clearfil AP-X (AP). All specimens were stored in distilled water at 37 °C for 24 h and 7 days. Scanning electron microscope (SEM) and energy dispersive X-ray (EDX) observations were performed to evaluate filler morphology and to detect the elements. The resin cements had a significant effect on the immediate µTBS (F = 22.59, p < 0.05) and after water storage µTBS (F = 22.83, p < 0.05). Significant differences ( p < 0.05) in the KHN between the tested materials were observed, and HL indicated the highest KHN when compared with PV. HL showed a combination of the regular-shaped filler and spherical-shaped filler within the matrix. Silicon was detected in HL from the EDX evaluation. HL exhibited better bonding performance and polymerization, which may have contributed to the improvement of the adhesive strength.