A Scalable and Surfactant-Free Emulsion Method for Producing Microbeads from Varied Biomass Feedstocks.

Despite national and international regulations, plastic microbeads are still widely used in personal care and consumer products (PCCPs). These exfoliants and rheological modifiers cause significant microplastic pollution in natural aquatic environments. Microbeads from nonderivatized biomass like cellulose and lignin can offer a sustainable alternative to these nondegradable microplastics, but processing this biomass into microbeads is challenging due to limited viable solvents and high biomass solution viscosities. To produce biomass microbeads of the appropriate size range for PCCPs (ca. 200-800 μm diameter) with shapes and mechanical properties comparable to those of commercial plastic microbeads, we used a surfactant-free emulsion/precipitation method, mixing biomass solutions in 1-ethyl-3-methylimidazolium acetate (EMImAc) with various oils and precipitating with ethanol. While yield of microbeads within the target size range highly depends on purification conditions, optimized protocols led to >90% yield of cellulose microbeads. Kraft lignin was then successfully incorporated into beads at up to 20 wt %; however, higher lignin contents result in emulsion destabilization unless surfactant is added. Finally, the microbead shape and surface morphology can be tuned using oils of varying viscosities and interfacial tensions. Dripping measurements and pendant drop tensiometry confirmed that the higher affinity of cellulose for certain oil/IL interfaces largely controlled the observed surface morphology. This work thus outlines how biomass composition, oil viscosity, and interfacial properties can be altered to produce more sustainable microbeads for use in PCCPs, which have desirable mechanical properties and can be produced over a wide range of shapes and surface morphologies.