Unexpected Crystallographic Phase Transformation in Nonstoichiometric SrUO4- x: Reversible Oxygen Defect Ordering and Symmetry Lowering with Increasing Temperature.

Gabriel L MurphyChun-Hai WangGeorge BeridzeZhaoming ZhangJustin A KimptonMaxim AvdeevPiotr M KowalskiBrendan James Kennedy
Published in: Inorganic chemistry (2018)
In situ synchrotron powder X-ray diffraction measurements have demonstrated that SrUO4 undergoes a reversible phase transformation under reducing conditions at high temperatures, associated with the ordering of oxygen defects resulting in a lowering of crystallographic symmetry. When substoichiometric rhombohedral α-SrUO4- x, in space group R3̅ m with disordered in-plane oxygen defects, is heated above 200 °C in a hydrogen atmosphere it undergoes a first order phase transformation to a (disordered) triclinic polymorph, δ-SrUO4- x, in space group P1̅. Continued heating to above 450 °C results in the appearance of superlattice reflections, due to oxygen-vacancy ordering forming an ordered structure δ-SrUO4- x. Cooling δ-SrUO4- x toward room temperature results in the reformation of the rhombohedral phase α-SrUO4- x with disordered defects, confirming the reversibility of the transformation. This suggests that the transformation, resulting from oxygen vacancy ordering, is not a consequence of sample reduction or decomposition, but rather represents a change in the energetics of the system. A strong reducing atmosphere is required to generate a critical amount of oxygen defects in α-SrUO4- x to enable the transformation to δ-SrUO4- x but once formed the transformation between these two phases can be induced by thermal cycling. The structure of δ-SrUO4- x at 1000 °C was determined using symmetry representation analysis, with the additional reflections indexed to a commensurate distortion vector k = ⟨1/4 1/4 3/4⟩. The ordered 2D layered triclinic structure of δ-SrUO4- x can be considered a structural distortion of the disordered 2D layered rhombohedral α-SrUO4- x structure through the preferential rearrangement of the in-plane oxygen vacancies. Ab initio calculations using density functional theory with self-consistently derived Hubbard U parameter support the assigned ordered defect superstructure model. Entropy changes associated with the temperature dependent short-range ordering of the reduced U species are believed to be important and these are discussed with respect to the results of the ab initio calculations.
Keyphrases
  • density functional theory
  • room temperature
  • molecular dynamics
  • mass spectrometry
  • ionic liquid
  • gold nanoparticles
  • data analysis
  • crystal structure