Synthesis, Characterization, and Bioactivity of Mesoporous Bioactive Glass Codoped with Zinc and Silver.

Due to the overconsumption of antimicrobials, antibiotic-resistant bacteria have become a critical health issue worldwide, especially methicillin-resistant S. aureus (MRSA) and vancomycin-resistant E. faecalis (VRE). Recently, many efforts have been made to load metals into bioactive glasses to enhance the multifunctionality of materials, such as antibacterial and osteoinductive functions. Zinc has been documented to stimulate the gene expression of various regulatory factors in bone cells. Meanwhile, previous studies have reported that silver and zinc could be a promising antibacterial combination with synergistic antimicrobial effects. Here, we sought to develop a biomaterial coreleasing zinc and silver, designated 80S-ZnAg, and to evaluate its antibacterial activity and biocompatibility. The textural analyses demonstrated different coreleasing patterns of zinc and silver for the materials. The chemical characterization revealed that the zinc in 80S-ZnAg could be the network modifier when its molar ratio was high, releasing more zinc; zinc could also be the network former when its molar ratio was low, showing an extremely low rate of release. However, the ICP results for 80S-Zn3Ag2 demonstrated up to 7.5 ppm of zinc and 67.6 ppm of silver. Among all the 80S-ZnAg materials, 80S-Zn3Ag2 demonstrated more marked antibacterial activity against MRSA and VRE than the others, with inhibition zones of 11.5 and 13.4 mm, respectively. The cytotoxicity assay exhibited nearly 90% cell viability at 20 mg/mL of 80-Zn3Ag2. Further clinical study is needed to develop an innovative biomaterial to address the issue of antibiotic resistance.