Effects of Fiber Loading on Mechanical Properties of Kenaf Nanocellulose Reinforced Nanohybrid Dental Composite Made of Rice Husk Silica.

Su Bing ShengRabihah AlawiYanti JohariNor Aidaniza Abdul MuttlibMohd Hazwan HussinDasmawati MohamadMohmed Isaqali Karobari
Published in: Journal of functional biomaterials (2023)
The innovation of nanocellulose as reinforcement filler in composites has been a topic of interest in the development of new biomaterials. The objective of this study was to investigate the mechanical properties of a nanohybrid dental composite made of rice husk silica and loaded with different percentages of kenaf nanocellulose. Kenaf cellulose nanocrystals (CNC) were isolated and characterized using a transmission electron microscope (TEM) (Libra 120, Carl Zeiss, Germany). The experimental composite was fabricated with fiber loadings of 1 wt%, 2 wt%, 3 wt%, 4 wt%, and 6 wt% silane-treated kenaf CNC, and subjected to a flexural and compressive strength test ( n = 7) using an Instron Universal Testing Machine (Shimadzu, Kyoto, Japan), followed by a scanning electron microscopic assessment of the flexural specimen's fracture surface using a scanning electron microscope (SEM) (FEI Quanta FEG 450, Hillsborough, OR, USA). Commercial composites Filtek Z350XT (3M ESPE, St. Paul, MN, USA), Neofil (Kerr Corporation, Orange, CA, USA) and Ever-X Posterior (GC Corporation, Tokyo, Japan) were used as a comparison. The average diameter of kenaf CNC under TEM was 6 nm. For flexural and compressive strength tests, one-way ANOVA showed a statistically significant difference ( p < 0.05) between all groups. Compared to the control group (0 wt%), the incorporation of kenaf CNC (1 wt%) into rice husk silica nanohybrid dental composite showed a slight improvement in mechanical properties and modes of reinforcement, which was reflected in SEM images of the fracture surface. The optimum dental composite reinforcement made of rice husk was 1 wt% kenaf CNC. Excessive fiber loading results in a decline in mechanical properties. CNC derived from natural sources may be a viable alternative as a reinforcement co-filler at low concentrations.
Keyphrases