Effect of Viscosity and Air Gap within the Spinneret on the Morphology and Mechanical Properties of Hollow-Fiber Polymer Membranes for Separation Performance.

Hollow-fiber membranes for nanofiltration were prepared from the blending of Poly (ethylene glycol) (PEG) with Poly (vinyl chloride) (PVC) with different PEG molecular weights (400 and 4000 g/mol) and PVC via a dry/wet spinning process. In the spinning process, the effects of air gap, wind-up speed, dope extrusion rate, and bore extrusion rate were examined. In addition, the different lengths of the center tube, which acted as the inner-side fiber diameter during the preparation of hollow-fiber membranes, were studied. This research was investigated in order to observe the morphological, dielectric, and dynamic mechanical thermal properties to identify a suitable preparation of a hollow-fiber membrane for feasible applications. The morphology of the PVC-580 blended PEG-400 5 weight percent hollow-fiber membrane was seen to have a dense skin on both the inner and outer fiber surface, along with a suitable dope viscosity. Moreover, it offered finger-like substructures that could provide a high applicable feed-stream permeability and selectivity. Finger-like substructures were present on the near inner fiber surface at the controlled center-tube length of 0.3 cm, more so than at the center tube of 1 cm. This was because the solvent and non-solvent in the lumen tube exchanged more quickly than they did in the coagulant bath. The effect of the wind-up speed during the spinning process was significantly influenced by an affordable hollow fiber that can be indicated by the drawing ratio ( λ ). It was found that the drawing ratio of 3.3 showed a thickness thinner than 2.6 and 2.0, respectively. In summary, a controlled wind-up speed, an acceptable dope viscosity, and-most importantly-an agglomerated time resulted in membrane preparation.