Two-Channel Indirect-Gap Photoluminescence and Competition between the Conduction Band Valleys in Few-Layer MoS 2 .

MoS 2 is a two-dimensional layered transition metal dichalcogenide with unique electronic and optical properties. The fabrication of ultrathin MoS 2 is vitally important, since interlayer interactions in its ultrathin varieties will become thickness-dependent, providing thickness-governed tunability and diverse applications of those properties. Unlike with a number of studies that have reported detailed information on direct bandgap emission from MoS 2 monolayers, reliable experimental evidence for thickness-induced evolution or transformation of the indirect bandgap remains scarce. Here, the sulfurization of MoO 3 thin films with nominal thicknesses of 30 nm, 5 nm and 3 nm was performed. All sulfurized samples were examined at room temperature with spectroscopic ellipsometry and photoluminescence spectroscopy to obtain information about their dielectric function and edge emission spectra. This investigation unveiled an indirect-to-indirect crossover between the transitions, associated with two different Λ and K valleys of the MoS 2 conduction band, by thinning its thickness down to a few layers.