Corrosive Studies of a Prosthetic Ni-Cr Alloy Coated with Ti(C,N) Type Layers.

Katarzyna BanaszekMarek MaślankaMichael SemenovLeszek Klimek
Published in: Materials (Basel, Switzerland) (2022)
Background: Investigating the general corrosion resistance of Ti(C,N) type coatings on a prosthetic nickel alloy in the aspect of their use as protective coatings on prosthetic and orthodontic elements. Methods: Five groups of Ni-Cr alloy samples covered with Ti(C,N) type coatings differing in their carbon and nitrogen contents were used for the tests. The reference group included alloy samples without coatings. The samples were held for 105 days (2520 h) in salt spray chambers and examined by means of the NSS (neutral salt spray) and SWAAT (sea water acetic acid test) tests. After the periods of 14, 28, 81 and 105 days, the samples were removed and weighed, and their weight losses were determined. Results: In the case of each type of Ti(C,N) coating, the mass loss was lower than the mass loss of a sample without a coating, which makes it possible to state that coatings improve the corrosion resistance. No significant differences in the resistance were observed between the particular coatings. The corrosion rate of the examined coatings is close to parabolic. Conclusions: Ti(C,N) type coatings improve the resistance of a prosthetic Ni-Cr alloy and can be used as protective coatings for prosthetic and orthodontic elements.
Keyphrases
  • body mass index
  • metal organic framework