Multifunctional Aspects of Mechanical and Electromechanical Properties of Composites Based on Silicone Rubber for Piezoelectric Energy Harvesting Systems.

Energy harvesting systems fabricated from rubber composite materials are promising due to their ability to produce green energy with no environmental pollution. Thus, the present work investigated energy harvesting through piezoelectricity using rubber composites. These composites were fabricated by mixing titanium carbide (TiC) and molybdenum disulfide (MoS 2 ) as reinforcing and electrically conductive fillers into a silicone rubber matrix. Excellent mechanical and electromechanical properties were produced by these composites. For example, the compressive modulus was 1.55 ± 0.08 MPa (control) and increased to 1.95 ± 0.07 MPa (6 phr or per hundred parts of rubber of TiC) and 2.02 ± 0.09 MPa (6 phr of MoS 2 ). Similarly, the stretchability was 133 ± 7% (control) and increased to 153 ± 9% (6 phr of TiC) and 165 ± 12% (6 phr of MoS 2 ). The reinforcing efficiency (R.E.) and reinforcing factor (R.F.) were also determined theoretically. These results agree well with those of the mechanical property tests and thus validate the experimental work. Finally, the electromechanical tests showed that at 30% strain, the output voltage was 3.5 mV (6 phr of TiC) and 6.7 mV (6 phr of MoS 2 ). Overall, the results show that TiC and MoS 2 added to silicone rubber lead to robust and versatile composite materials. These composite materials can be useful in achieving higher energy generation, high stretchability, and optimum stiffness and are in line with existing theoretical models.