Novel and Accessible Physical Recycling for Expanded Polystyrene Waste with the Use of Acetone as a Solvent and Additive Manufacturing (Direct Ink-Write 3D Printing).

The current high production of plastics has prompted the exploration of alternative pathways to facilitate recycling, aiming for a progressively sustainable society. This paper presents an alternative and affordable technology for treating waste expanded polystyrene (EPS) mixed with acetone in a 100:1 volume ratio to be used as 3D printing ink for Direct Ink Write technology. In order to optimize the printing parameters, a comprehensive study was conducted, evaluating different needle diameters, printing speeds, and bed temperature values to achieve homogenous pieces and a highly repeatable 3D printing process. Results showed that the main optimum printing parameters were using needles with diameters of 14 to 16 G and printing speeds ranging from 2 to 12 mm/s, which were found to yield the most uniform ribbons. Increasing the bed temperature, despite favoring acetone evaporation, led to the generation of more heterogeneous structures due to void growth inside the printed ribbons. Thus, employing room temperature for the bed proved to be the optimal value. Lastly, a comparative study between the starting material and the EPS after the printing process was conducted using FTIR-ATR and GPC analyses, ensuring the preservation of the original polymer's integrity during physical recycling.