Boosting the Cycle Performance of Iron Trifluoride Based Solid State Batteries at Elevated Temperatures by Engineering the Cathode Solid Electrolyte Interface.

Iron trifluoride (FeF 3 ) is attracting tremendous interest due to its lower cost and the possibility to enable higher energy density in lithium-ion batteries. However, its cycle performance deteriorates rapidly in less than 50 cycles at elevated temperatures due to cracking of the unstable cathode solid electrolyte interface (CEI) followed by active materials dissolution in liquid electrolyte. Herein, by engineering the salt composition, the Fe 3 O 4 -type CEI with the doping of boron (B) atoms in a polymer electrolyte at 60 °C is successfully stabilized. The cycle life of the well-designed FeF 3 -based composite cathode exceeds an unprecedented 1000 cycles and utilizes up to 70% of its theoretical capacities. Advanced electron microscopy combined with density functional theory (DFT) calculations reveal that the B in lithium salt migrates into the cathode and promotes the formation of an elastic and mechanic robust boron-contained CEI (BOR-CEI) during cycling, by which the durability of the CEI to frequent cyclic large volume changes is significantly enhanced. To this end, the notorious active materials dissolution is largely prohibited, resulting in a superior cycle life. The results suggest that engineering the CEI such as tuning its composition is a viable approach to achieving FeF 3 cathode-based batteries with enhanced performance.