Materials characterization of TiO 2 nanotubes decorated by Au nanoparticles for photoelectrochemical applications.

The structural and chemical modification of TiO 2 nanotubes (NTs) by the deposition of a well-controlled Au deposit was investigated using a combination of X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), Scanning Transmission Electron Microscopy (STEM), Raman measurements, UV-Vis spectroscopy and photoelectrochemical investigations. The fabrication of the materials focused on two important factors: the deposition of Au nanoparticles (NPs) in UHV (ultra high vacuum) conditions (1-2 × 10 -8 mbar) on TiO 2 nanotubes (NTs) having a diameter of ∼110 nm, and modifying the electronic interaction between the TiO 2 NTs and Au nanoparticles (NPs) with an average diameter of about 5 nm through the synergistic effects of SMSI (Strong Metal Support Interaction) and LSPR (Local Surface Plasmon Resonance). Due to the formation of unique places in the form of "hot spots", the proposed nanostructures proved to be photoactive in the UV-Vis range, where a characteristic gold plasmonic peak was observed at a wavelength of 580 nm. The photocurrent density of Au deposited TiO 2 NTs annealed at 650 °C was found to be much greater (14.7 μA cm -2 ) than the corresponding value (∼0.2 μA cm -2 ) for nanotubes in the as-received state. The IPCE (incident photon current efficiency) spectral evidence also indicates an enhancement of the photoconversion of TiO 2 NTs due to Au NP deposition without any significant change in the band gap energy of the titanium dioxide ( E g ∼3.0 eV). This suggests that a plasmon-induced resonant energy transfer (PRET) was the dominant effect responsible for the photoactivity of the obtained materials.