Study of a Novel Electrochromic Device with Crystalline WO 3 and Gel Electrolyte.
Wanyu ChenGuixia ZhangLili WuSiyuan LiuMeng CaoYing YangYong PengPublished in: Polymers (2022)
Most ECDs are coated with an electrochromic material on the transparent conductive oxide (TCO) substrate. A novel electrochromic device (ECD), having a variable optical performance, was prepared by using tungsten foil as a substrate in this study. It was found that the WO 3 discoloration layer, having a monoclinic phase crystalline structure made of 600 °C calcined, had optimum charge transmission performance with PADA gel polymer electrolyte. Ionic conductivity of PADA gel polymer electrolyte was 2.3 × 10 -3 S cm -1 at -20 °C, and it was possible to help Li + to implement embedding and extraction from WO 3 even in low-temperature conditions. The colored time (t c ) and the bleached time (t b ) of the electrochromic device were 15 s and 26 s, and it showed yellowish-brown in the colored state and navy blue in the bleached state. The ECD (WO 3 -600) exhibited good cycle stability reach at least 150 times.