Reversible and repeatable phase transition at a negative temperature regime for doped and co-doped spin coated mixed valence vanadium oxide thin films.

Smooth, uniform mixed valance vanadium oxide (VO) thin films are grown on flexible, transparent Kapton and opaque Al6061 substrates by the spin coating technique at a constant rpm of 3000. Various elements e.g. , F, Ti, Mo and W are utilized for doping and co-doping of VO. All the spin coated films are heat treated in a vacuum. Other than the doping elements the existence of only V 4+ and V 5+ species is noticed in the present films. Transmittance as a function of wavelength and the optical band gap are also investigated for doped and co-doped VO thin films grown on a Kapton substrate. The highest transparency (∼75%) is observed for the Ti, Mo and F ( i.e. , Ti-Mo-FVO) co-doped VO system while the lowest transparency (∼35%) is observed for the F ( i.e. , FVO) doped VO system. Thus, the highest optical band gap is estimated as 2.73 eV for Ti-Mo-FVO and the lowest optical band gap ( i.e. , 2.59 eV) is found for the FVO system. The temperature dependent phase transition characteristics of doped and co-doped VO films on both Kapton and Al6061 are studied by the differential scanning calorimetry (DSC) technique. Reversible and repeatable phase transition is noticed in the range of -24 to -26.3 °C.