Closed-loop recyclable and biodegradable thioester-based covalent adaptable networks.

Closed-loop recyclable and biodegradable aliphatic covalent adaptable networks (CANs) based on dynamic β-CO thioester linkages that exhibit a service temperature beyond 100 °C are reported. These CANs possessing tensile strength and modulus values of up to 0.3 and 3 MPa, respectively, effectively undergo stress relaxation above 100 °C. The samples exhibit creep resistance ability and low hysteresis loss, and are repeatedly reprocessable at 120 °C. These CANs are depolymerizable to monomers under mild conditions and lose notable mechanical strength (92.4%) and weight (76.5%) within ∼35 days under natural biodegradation conditions.