A comparative study of α-Ni(OH) 2 and Ni nanoparticle supported ZIF-8@reduced graphene oxide-derived nitrogen doped carbon for electrocatalytic ethanol oxidation.

Ethanol electrooxidation is an important reaction for fuel cells, however, the major obstacle to ethanol electrocatalysis is the splitting of the carbon-carbon bond to CO 2 at lower overpotentials. Herein, a ZIF-8@graphene oxide-derived highly porous nitrogen-doped carbonaceous platform containing zinc oxide was attained for supporting a non-precious Ni-based catalyst. The support was doped with the disordered α-phase Ni(OH) 2 NPs and Ni NPs that are converted to Ni(OH) 2 through potential cycling in alkaline media. The Ni-based catalysts exhibit high electroactivity owing to the formation of the NiOOH species which has more unpaired d electrons that can bond with the adsorbed species. From CV curves, the EOR onset potential of the α-Ni(OH) 2 /ZNC@rGO electrode is strongly shifted to negative potential ( E onset = 0.34 V) with a high current density of 8.3 mA cm -2 relative to Ni/ZNC@rGO. The high catalytic activity is related to the large interlayer spacing of α-Ni(OH) 2 which facilitates the ion-solvent intercalation. Besides, the porous structure of the NC and the high conductivity of rGO facilitate the kinetic transport of the reactants and electrons. Finally, the catalyst displays a high stability of 92% after 900 cycles relative to the Ni/ZNC@rGO and commercial Pt/C catalysts. Hence, the fabricated α-Ni(OH) 2 /ZNC@rGO catalyst could be regarded as a potential catalyst for direct EOR in fuel cells.