The Effect of Macromonomer Surfactant Microstructure on Aqueous Polymer Dispersion and Derived Polymer Film Properties.

Water-borne coatings were prepared from poly(methyl methacrylate- co -butyl acrylate) latexes using different methacrylic acid containing macromonomers as stabilizers, and their physical properties were determined. The amphiphilic methacrylic acid macromonomers containing methyl, butyl, or lauryl methacrylate as hydrophobic comonomers were synthesized via catalytic chain transfer polymerization to give stabilizers with varying architecture, composition, and molar mass. A range of latexes of virtually the same composition was prepared by keeping the content of methacrylic acid groups during the emulsion polymerization constant and by only varying the microstructure of the macromonomers. These latexes displayed a range of rheological behaviors: from highly viscous and shear thinning to low viscous and Newtonian. The contact angles of the resulting coatings ranged from very hydrophilic (<10°) to almost hydrophobic (88°), and differences in hardness, roughness, and water vapor sorption and permeability were found.