Controllable synthesis of few-layer ammoniated 1T'-phase WS 2 as an anode material for lithium-ion batteries.

Two-dimensional transition metal dichalcogenide (TMDC) nanosheets have received significant attention as anode materials for lithium-ion batteries, especially in their metallic 1T/1T' phase. However, controllable synthesis of few-layer 1T/1T' phase is still a challenge. In the present study, we report a facile two-step hydrothermal method to controllably synthesize few-layer 1T'-phase WS 2 . By tuning the redox-temperature of (NH 4 ) 2 WS 4 from 160 to 200 °C, the thickness of 1T'-phase WS 2 can be adjusted from 4-6 to 20 layers. A higher reversible capacity is achieved in 1T'-phase WS 2 with a smaller thickness, but the cycling stability decreases due to the lower crystallinity. The 1T'-phase WS 2 synthesized by reduction of (NH 4 ) 2 WS 4 at 180 °C shows a moderate thickness of 10 layers and crystallinity, exhibiting the optimal Li-ion storage properties, i.e. a reversible capacity of 855.9 mA h g -1 at 100 mA g -1 and a good rate performance of 354.4 mA h g -1 at 5000 mA g -1 . These results provide new insights into understanding the impacts of layer number on the Li-ion storage properties of 1T'-phase WS 2 .