Greatly enhanced hole collection of MoO x with top sub-10 nm thick silver films for gridless and flexible crystalline silicon heterojunction solar cells.

Greatly enhanced hole collection of MoO x is demonstrated experimentally with a top sub-10 nm thick Ag film, allowing for an efficient dopant-free contacted crystalline silicon (c-Si) heterojunction solar cell without a front grid electrode. With the removal of shadows induced by the front grid electrode, the gridless solar cell with the MoO x /Ag hole-selective contact (HSC) shows an increment of ∼8% in its power conversion efficiency (PCE) due to the greatly improved short-circuit current density ( J sc ) as well as the almost undiminished fill factor (FF) and open-circuit voltage ( V oc ), while the gridless solar cells with the conventional MoO x /ITO and pure MoO x HSCs exhibit ∼20% and ∼43% degradations in PCE due to the overwhelming decrease in their FF and J sc , respectively. Through systematic characterizations and analyses, it is found that the ultrathin Ag film (more conductive than ITO) provides an additional channel for photogenerated holes to transport on MoO x , contributing to the great enhancement in the hole collection and the great suppression of the shunt loss in the gridless solar cells. A 50 μm thick gridless c-Si heterojunction solar cell with the MoO x /Ag HSC is 75% thinner but is 86% efficient compared to its 200 μm thick counterpart (while the 50 μm thick gridless solar cell with the MoO x /ITO HSC is much less efficient). It is over 82% efficient after being bent to a curvature radius as small as 4 mm, also showing superior mechanical flexibility to its counterpart with the MoO x /ITO HSC. Our MoO x /Ag double-layer HSC can be easily fabricated through thermal evaporation without breaking the vacuum, saving both the time and cost of the fabrication of the whole device. Therefore, this work provides a guide for the design of efficient HSCs for high-efficiency, low-cost, and flexible solar cells.