Investigation of Multiple Shape Memory Behaviors, Thermal and Physical Properties of Benzoxazine Blended with Diamino Polysiloxane.

In this research, benzoxazine (BA-a) and diamino polysiloxane (PSX750) blends were prepared at 0-50 wt% of BA-a. The interactions between two polymeric components were investigated via a Fourier Transform Infrared Spectrometer (FT-IR). The thermal properties of the blends were also determined with Dynamic Mechanical Analyzer (DMA) and Thermogravimetric Analyzer (TGA). The mechanical properties and shape memory behaviors of the blends were also investigated. The FTIR spectra exhibited the shift of the peak from 1672 to the range of 1634-1637 cm -1 , which could be identified as hydrogen bonds between two polymeric domains at the contents from 30 to 50 wt%. The DMA thermograms revealed two glass transition temperatures, which could indicate a partially miscible system. The char yield values were increased, while the decomposition temperatures were decreased with an increasing benzoxazine content. Interestingly, the blends at the contents of 10 and 20 wt% presented dual-shape memory behaviors, whereas triple- or multiple-shape memory behaviors were observed with benzoxazine contents of 30 to 50 wt%. For the high-temperature recovery state, a shape memory ratio of 97.5% with a recovery time of 65 s and a shape fixity ratio of 66.7% was recorded at the content of 50 wt%. For the low-temperature recovery state, a shape recovery ratio of 98.9% was observed at the same content. Moreover, the values of the recovery ratio for four shape-recovery cycles revealed multiple shape memory behaviors with high recovery ratios in the range of 95-98%.