Aqueous Solution-Grown Crystalline Phosphorus Doped Indium Oxide for Thin-Film Transistors Applications.

Solution-grown indium oxide (In 2 O 3 ) based thin-film transistors (TFTs) hold good prospects for emerging advanced electronics due to their excellent mobility, prominent transparency, and possibility of low-cost and scalable manufacturing; however, pristine In 2 O 3 TFTs suffer from poor switching characteristics due to intrinsic oxygen-vacancy-related defects and require external doping. According to Shanmugam's theory, among potential dopants, phosphorus (P) has a large dopant-oxygen bonding strength (E M-O ) and high Lewis acid strength (L) that would suppress oxygen-vacancy related defects and mitigate dopant-induced carrier scattering; however, P-doped In 2 O 3 (IPO) TFTs have not yet been demonstrated. Here, we report aqueous solution-grown crystalline IPO TFTs for the first time. It is suggested that the incorporation of P could effectively inhibit oxygen-vacancy-related defects while maintaining high mobility. This work experimentally demonstrates that dopant with high E M-O and L is promising for emerging oxide TFTs.