Improvement of the Oxygen Storage/Release Speed of YBaCo4O7+δ Synthesized by a Glycine-Complex Decomposition Method.
Tingru ChenTakuya HasegawaYusuke AsakuraMasato KakihanaTeruki MotohashiShu YinPublished in: ACS applied materials & interfaces (2021)
The present study explores the oxygen storage capacity of YBaCo4O7+δ prepared by a glycine-complex decomposition method. We reported for the first time that the YBaCo4O7+δ sample was successfully synthesized at such a low temperature of 800 °C by this method. The YBCO-800 N sample exhibited a faster oxygen absorption/desorption speed than that of high calcination temperature samples, and the time required for complete oxygen storage/release was 5 and 6 min at 360 °C, respectively. Moreover, the superior performance observed for this product in the temperature swing adsorption process makes it a promising candidate in oxygen production technologies. This research demonstrated that the glycine-complex decomposition method is an effective method for improving the oxygen storage property of YBaCo4O7+δ and provides a new insight into designing other novel oxygen storage materials.
Keyphrases